몰리브덴
The ability of molybdenum to form ferrite is comparable to that of chromium. Molybdenum also promotes intermetallic compounds in stainless steels. In order to maintain a single austenite structure in austenitic stainless steel, the content of nickel, nitrogen, manganese and other austenite forming elements should be increased with the increase of molybdenum content in steel. Molybdenum has obvious solution strengthening effect in austenitic stainless steel. With the increase of molybdenum content, the high temperature rupture strength and crzm eep resistance of steel are greatly improved. Therefore, molybdenum containing stainless steel is often used at higher temperatures. The higher the molybdenum content, the worse the hot workability. The main role of molybdenum in austenitic stainless steel is to expand its application scope, improve the corrosion resistance of steel in reducing medium, and improve the pitting corrosion resistance and crevice corrosion resistance of steel. However, in oxidizing medium, the effect of molybdenum is harmful. When the molybdenum content is more than 3.5%, the corrosion rate in HNO3 increases sharply.
구리
오스테 나이트 스테인리스 스틸에서 구리의 역할은 냉 작업 경계 경향을 크게 줄이고 냉 작업 형성성을 향상시키는 것입니다. 구리와 몰리브덴의 조합은 환원 매체에서 오스테 나이트 스테인레스 스틸의 내식성을 더욱 향상시킬 수있다. 오스테 나이트 스테인리스 스틸에서, 구리 함량의 증가에 따라 특정 범위의 구리 함량에서 강철의 강도가 감소하고 가소성이 증가하며 변형 강화 지수 N이 감소합니다. 일부 오스테 나이트 스테인리스 강 (303304 및 기타 강)은 차가운 작동 압축 균열 경향이 있으며 구리의 첨가는 냉간 형성성을 향상시킬 수 있습니다. 구리는 특히 오스테 나이트 스테인레스 스틸의 니켈 함량이 낮을 때 강철의 뜨거운 작업성을 크게 감소시킵니다. 따라서 강철의 구리 함량이 높으면 그에 따라 니켈 함량도 증가해야합니다. 구리는 오스테 나이트 스테인리스 스틸의 황산, 인산 및 기타 환원 배지에 대한 부식성을 크게 향상시킬 수 있습니다. 구리와 몰리브덴이 복합 합금에 사용될 때, 효과가 더 두드러집니다.
망간
CR NI 오스테 나이트 스테인리스 스틸에서, 망간 함량은 일반적으로 2%를 초과하지 않으며 생산에서 1.5%로 제어됩니다. 니켈 스테인레스 스틸의 후기 발달에서, 망간은 중요한 합금 요소가되며, 이는 주로 질소 및 일정량의 니켈과 안정한 오스테 나이트를 형성합니다.
망간 함량이 2%미만인 경우, 망간 함량의 변화는 오스테 나이트의 안정성을 포함하여 일반적인 크롬 니켈 스테인레스 스틸의 구조에 명백한 영향을 미치지 않습니다. 망간은 CR NI 오스테 나이트 스테인레스 스틸의 열가소성을 향상시킬 수 있습니다.
후 시간 : 12 월 - 29 - 2022