オーステナイトステンレスの微細構造と特性に対するモリブデン、銅、マンガンの効果

モリブデン

The ability of molybdenum to form ferrite is comparable to that of chromium. Molybdenum also promotes intermetallic compounds in stainless steels. In order to maintain a single austenite structure in austenitic stainless steel, the content of nickel, nitrogen, manganese and other austenite forming elements should be increased with the increase of molybdenum content in steel. Molybdenum has obvious solution strengthening effect in austenitic stainless steel. With the increase of molybdenum content, the high temperature rupture strength and crzm eep resistance of steel are greatly improved. Therefore, molybdenum containing stainless steel is often used at higher temperatures. The higher the molybdenum content, the worse the hot workability. The main role of molybdenum in austenitic stainless steel is to expand its application scope, improve the corrosion resistance of steel in reducing medium, and improve the pitting corrosion resistance and crevice corrosion resistance of steel. However, in oxidizing medium, the effect of molybdenum is harmful. When the molybdenum content is more than 3.5%, the corrosion rate in HNO3 increases sharply.

銅

オーステナイトのステンレス鋼における銅の役割は、冷たい作業の硬化傾向を大幅に減らし、寒い作業の形成性を向上させることです。銅とモリブデンの組み合わせは、培地の還元においてオーステナイトステンレス鋼の耐食性をさらに改善することができます。オーステナイトのステンレス鋼では、銅含有量の増加に伴い、特定の範囲の銅含有量において、鋼の強度が低下し、可塑性が増加し、ひずみ強化指数nが減少します。一部のオーステナイトステンレス鋼（303304およびその他の鋼）は、冷たい作業圧縮亀裂の傾向があり、銅を添加すると冷たい形成性が向上する可能性があります。銅は、特にオーステナイトステンレス鋼のニッケル含有量が低い場合、鋼の熱い作業性を大幅に低下させます。したがって、鋼の銅含有量が高い場合、ニッケル含有量もそれに応じて増加する必要があります。銅は、硫酸、リン酸、その他の還元培地に対するオーステナイトステンレス鋼の耐食性を大幅に改善できます。銅とモリブデンが複合合金に使用される場合、効果はより顕著です

マンガン

Cr Ni Austeniticステンレス鋼では、マンガンの含有量は一般に2％を超えず、ほとんどが生産量1.5％で制御されています。ニッケルステンレス鋼のその後の発達では、マンガンは重要な合金要素になり、主に窒素と一定量のニッケルを含む安定したオーステナイトを形成します。

マンガンの含有量が2％未満の場合、マンガン含有量の変化は、オーステナイトの安定性を含む一般的なクロムニッケルステンレス鋼の構造に明らかな影響を与えません。マンガンは、Cr niオーステナイトステンレス鋼の熱可塑性を改善できます。